sg iron properties ASTM A395 cast iron foundry railing parts 65 45 12 ductile iron parts
Production process: green sand molding, pre-coated sand molding and resin sand molding which can produce iron castings from 50 gram to 2000 kilograms
Machining process: CNC machine, machining center, lathe, mill machine, drill machine, etc.
Surface treatment process: paint coating, electrophoretic coating, electrogalvanizing coating, black oxide coating, powder coating, etc.
Product Material and Uses
Normally produce with gray iron HT200, HT250, ductile iron 65-45-12, 60-40-18, 80-55-06, 80-60-03, etc.
The ductile iron casting products are widely used for Auto-cars, trains, trucks, vehicle components, mining machinery components, agricultural machinery parts, textile machinery parts, construction machinery parts, etc.
What is Ductile Iron?
Ductile iron is a modern iteration of cast iron. Cast iron and ductile iron have contrasting physical properties caused by differences in their microstructures.
The graphite and carbon contained in cast iron occur as flakes; cast iron exhibits positive compressive load capabilities, but tensile loading above its natural tensile strength can cause cracks to form and propagate rapidly out from stress points within the flaked graphite microstructure. As a result, cast iron has virtually no elongation. It is a brittle material, and therefore limited in its use in tensile and shock loading applications.
The graphite within ductile iron occurs as spheroids, so it is sometimes referred to as spheroidal graphite. Similarly, the term nodular iron stems from the fact that the carbon contained in ductile iron is held in the form of nodules. This unique microstructure causes ductile iron to withstand bending and shock loading far better than traditional cast iron.